Dane techniczne
Obrabialność materiałów
Stal automatowa
AISI 1212
W.Nr: 1.0711
9S20
St3
Twardość: 160HB
100% obrabialności
| STAL WĘGLOWA | OBRABIALNOŚĆ |
|---|---|
| 1015 | 72% |
| 1018 | 78% |
| 1020 | 72% |
| 1022 | 78% |
| 1030 | 70% |
| 1040 | 64% |
| 1042 | 64% |
| 1050 | 54% |
| 1095 | 42% |
| 1117 | 91% |
| 1137 | 72% |
| 1141 | 70% |
| 1141 wyżarzone | 81% |
| 1144 | 76% |
| 1144 wyżarzone | 85% |
| 1144 odporność na naprężenia | 83% |
| 1212 | 100% |
| 1213 | 136% |
| 12L14 | 170% |
| 1215 | 136% |
| STALE NARZĘDZIOWE | OBRABIALNOŚĆ |
|---|---|
| A-2 | 42% |
| A-6 | 33% |
| D-2 | 27% |
| D-3 | 27% |
| M-2 | 39% |
| 0-1 | 42% |
| 0-2 | 42% |
| STALE STOPOWE STAL | OBRABIALNOŚĆ |
|---|---|
| 2355 wyżarzone | 70% |
| 4130 wyżarzone | 72% |
| 4140 wyżarzone | 66% |
| 4142 wyżarzone | 66% |
| 41L42 wyżarzone | 77% |
| 4150 wyżarzone | 60% |
| 4340 wyżarzone | 57% |
| 4620 | 66% |
| 4820 wyżarzone | 49% |
| 52100 wyżarzone | 40% |
| 6150 wyżarzone | 60% |
| 8620 | 66% |
| 86L20 | 77% |
| 9310 wyżarzone | 51% |
| ŻELIWO KULKOWE | OBRABIALNOŚĆ |
|---|---|
| 60-40-18 wyżarzone | 61% |
| 65-45-12 wyżarzone | 61% |
| 80-55-06 | 39% |
| STOPY ALUMINIUM I MAGNEZU | OBRABIALNOŚĆ |
|---|---|
| Aluminium, ciągnione na zimno | 360% |
| Aluminium, odlew | 450% |
| Aluminium, odlew ciśnieniowy | 76% |
| Magnez, ciągniony na zimno | 480% |
| Magnez, odlew | 480% |
| STALE NIERDZEWNE I SUPER STOPY | OBRÓBKA |
|---|---|
| 302 wyżarzone | 45% |
| 303 wyżarzone | 78% |
| 304 wyżarzone | 45% |
| 316 wyżarzone | 45% |
| 321 wyżarzone | 36% |
| 347 wyżarzone | 36% |
| 410 wyżarzone | 54% |
| 416 wyżarzone | 110% |
| 420 wyżarzone | 45% |
| 430 wyżarzone | 54% |
| 431 wyżarzone | 45% |
| 440A | 45% |
| 15-5PH condition A | 48% |
| 17-4PH condition A | 48% |
| A286 aged | 33% |
| Hastelloy X | 19% |
| ŻELIWO SZARE | OBRABIALNOŚĆ |
|---|---|
| ASTM class 20 wyżarzone | 73% |
| ASTM class 25 | 55% |
| ASTM class 30 | 48% |
| ASTM class 35 | 48% |
| ASTM class 40 | 48% |
| ASTM class 45 | 36% |
| ASTM class 50 | 36% |